Processing Conditions

Typical processing conditions for M500026T are: Barrel temperature: 180 – 230°C Mold temperature: 15 -60 °C Injection pressure: 600 – 1000 Bar.

Health And Safety Considerations And Precautions

M500026T is suitable for Food contact application. Detailed information is provided in relevant Material Safety Datasheet and for additional specific information please contact SABIC local representative for certificate.

DISCLAIMER

This product is not intended for and must not be used in any pharmaceutical/medical applications.

Storage And Handling

Polyethylene resin should be stored in a manner to prevent a direct exposure to sunlight and/or heat. The storage area should also be dry and preferably do not exceed 50°C. SABIC would not give warranty to bad storage conditions which may lead to quality deterioration such as color change, bad smell and inadequate product performance. It is advisable to process PE resin within 6 months after delivery.

Typical Property Values

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Density	926	kg/m³	926
Melt Flow Rate (MFR)
at 190℃ and 2.16 kg	50	g/10 min	ASTM D1238
MECHANICAL PROPERTIES
Flexural Strength	9	MPa	ASTM D790
Flexural Modulus (1% Secant)	200	MPa	ASTM D790 A
Izod Impact Strength	500	J/m	ASTM D256
Hardness (Shore D)	50	–	ASTM D2240F
ESCR (10% Igepal), F50	3	Hrs	ASTM D1693B
ESCR (100% Igepal), F50	6	Hrs	ASTM D1693B
Tensile stress at yield (50mm/min)	10	MPa	ISO 527-2 1A
Tensile stress at break (5mm/min)	12	MPa	ISO 527-2 1A
Tensile strain at break (5mm/min)	>100	%	ISO 527-2 1A
THERMAL PROPERTIES
Vicat Softening Point	Vicat Softening Point 88	℃	ASTM D1525
Brittleness Temperature	<-75	℃	ASTM D746