SABIC FI0851P
SABIC FI0851P is a high-molecular-weight, high-density polyethylene resin developed for blown-film applications. It offers excellent processability, high film stiffness, good impact strength, and reliable toughness.
SABIC® Brand | HDPE Blown Film Grade | MFR 0.05 g/10 min at 190°C / 2.16 kg | Origin: Saudi Arabia
Description
SABIC FI0851P is a high-molecular-weight, high-density polyethylene resin designed for blown-film extrusion. Its broad molecular-weight distribution provides good processability and supports stable film production.
Films manufactured from this grade provide high stiffness, good impact performance, toughness, and mechanical strength, making the grade suitable for a range of thin-film and bag applications.
Applications
- Shopping bags
- T-shirt bags
- Grocery sacks
- Refuse bags
- Bags-on-roll
- Thin blown-film products
Key Characteristics
Typical Property Values
The following values represent typical properties reported for SABIC FI0851P.
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Polymer Properties | |||
| Melt Mass-Flow Rate at 190°C / 21.6 kg | 9 | g/10 min | ASTM D1238 |
| Melt Mass-Flow Rate at 190°C / 2.16 kg | 0.05 | g/10 min | ASTM D1238 |
| Density | 0.951 | g/cm³ | ASTM D792 |
| Film Mechanical Properties | |||
| Tensile Stress at Yield, MD | 35 | MPa | ASTM D882 |
| Tensile Stress at Yield, TD | 30 | MPa | ASTM D882 |
| Tensile Stress at Break, MD | 50 | MPa | ASTM D882 |
| Tensile Stress at Break, TD | 48 | MPa | ASTM D882 |
| Tensile Strain at Break, MD | 490 | % | ASTM D882 |
| Tensile Strain at Break, TD | 500 | % | ASTM D882 |
| Elmendorf Tear Strength, MD | 17 | gf | ASTM D1922 |
| Elmendorf Tear Strength, TD | 30 | gf | ASTM D1922 |
| Dart Impact | 340 | g | ASTM D1709 |
| Thermal Properties | |||
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
Technical values are typical and should not be treated as guaranteed specifications. Final properties, testing conditions, and product compliance should be confirmed through the latest manufacturer-issued TDS and the batch COA before purchase.
Processing
SABIC FI0851P is intended for blown-film extrusion. Processing temperatures, blow-up ratio, film thickness, output rate, and cooling conditions should be adjusted according to the extrusion equipment and finished-film requirements.
The latest manufacturer processing recommendations should be followed before commercial production.
Storage and Handling
Store the resin in its original packaging in a clean, dry, and well-ventilated area. Protect the material from direct sunlight, excessive heat, moisture, dust, and other sources of contamination.
Storage conditions and maximum recommended storage duration should be confirmed through the current manufacturer documentation.