Applications

• Shopping bag

• Garbage bag

• Industrial liner

Processing Conditions

Typical processing conditions for FI0851P are:

Melt temperature: 250°C

Mold temperature: 15-60°C

Injection pressure: 600 – 1000 Bar

Storage And Handling

Polyethylene material should be stored in a manner to prevent a direct exposure to sunlight and/or heat. The storage area should also be dry and preferably don’t exceed 50°C. SABIC would not give warranty to bad storage conditions which may lead to quality deterioration such as color change, bad smell and inadequate product performance. It is advisable to process PE resin within 6 months after delivery.

Disclaimer

Any sale by SABIC, its subsidiaries and affiliates (each a “seller”), is made exclusively under seller’s standard conditions of sale (available upon request) unless agreed otherwise in writing and signed on behalf of the seller. While the information contained herein is given in good faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each customer must determine the suitability of seller materials for the customer’s particular use through appropriate testing and analysis. No statement by seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.

Typical Property Values

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190 °C and 21 kg	8	dg/min	ASTM D1238
at 190 °C and 2.16 kg	0.05	dg/min	ASTM D1238
Density
Density	0.951	g/cm³	ASTM D792
MECHANICAL PROPERTIES
Tensile test
stress strength @ yield, MD	35	MPa	ASTM D882
stress strength @ yield, TD	30	MPa	ASTM D882
stress strength @ yield, MD	50	MPa	ASTM D882
stress strength @ yield, TD	48	MPa	ASTM D882
stress Elongation @ Break, MD	490	%	ASTM D882
stress Elongation @ Break, TD	500	%	ASTM D882
Elmendorf Tear Strength, MD	17	gf	ASTM D1922
Elmendorf Tear Strength, TD	30	gf	ASTM D1922
Dart Drop Impact	340	g	ASTM D1709
THERMAL PROPERTIES
Vicat Softening Temperature
Vicat Softening Temperature	126	°C	ASTM D1525